| Chemical Component | Poly 1.4-butanediol bis (p-aminobenzoate) |
| CAS NO. | 54667-43-5 |
| Appearance | Amber transparent viscous liquid |
| Odour | Slightly ammonia odor |
| Viscosity | 3000-4000mPa.s(40°C) |
| Moisture Content | <500ppm |
| Proportion | 0.98/cm3(25°C) |
| Amino equivalent content | 430-460 |
| Product Structure |  |
Product Feature
It is liquid at room temperature and has excellent site remediation applications. There is no need to prepare the prepolymer first. It can be directly mixed with diisocyanate and then reacted to prepare the required product. The overall physical properties of the product made are similar to those of the traditional thermocuring system with MDI prepolymer. Meanwhile, its performance will be superior to these MDI/ diol thermosetting elastomer systems. When operated in a natural environment, Amine-HCA™P-650 based elastomers have a very low shrinkage rate.
Application Fields
Coatings
Adhesives
Sealants and spray systems
Cast prototypes and elastomers
| Chemical Component | Poly 1.4-butanediol bis (p-aminobenzoate) |
| CAS NO. | 54667-43-5 |
| Appearance | Amber transparent viscous liquid |
| Odour | Slightly ammonia odor |
| Viscosity | 3000-4000mPa.s(40°C) |
| Moisture Content | <500ppm |
| Proportion | 0.98/cm3(25°C) |
| Amino equivalent content | 430-460 |
| Product Structure | |
Product Feature
It is liquid at room temperature and has excellent site remediation applications. There is no need to prepare the prepolymer first. It can be directly mixed with diisocyanate and then reacted to prepare the required product. The overall physical properties of the product made are similar to those of the traditional thermocuring system with MDI prepolymer. Meanwhile, its performance will be superior to these MDI/ diol thermosetting elastomer systems. When operated in a natural environment, Amine-HCA™P-650 based elastomers have a very low shrinkage rate.
Application Fields
Coatings
Adhesives
Sealants and spray systems
Cast prototypes and elastomers